Abstract(#br)In this work, micro-nanostructure polydimethylsiloxane/silicon dioxide (PDMS/SiO 2 ) composite coatings were fabricated on the surface of magnesium alloys with two different sizes of SiO 2 nanoparticles by a simple painting method. The effects of the proportion of 40 nm and 50–250 nm SiO 2 on the wettability, wear and corrosion performance of the composite coatings were investigated.

Abstract(#br)Ice accretion on airplane surfaces, power lines, or wind turbines can cause operational difficulties and disastrous events. Great efforts have been made to develop environmentally-friendly anti-icing or deicing surfaces over the last several decades, but a high-efficient, robust, and energy-saving surface for both anti-icing and deicing still remains a challenge.

摘要( # br )超疏水薄膜在应用中的最大障碍之一是其较差的机械阻力。本研究将粗糙电沉积的SiO2 ( E-SiO2 )薄膜与表面能较低的耐用聚二甲基硅氧烷( PDMS )聚合物结合，在温和钢( MS )上构建了用于腐蚀防护的鲁棒超疏水SiO2薄膜。结果表明，PDMS含量对最终薄膜的微观形貌、润湿性、粗糙度和耐磨性有较大影响。EIS测试结果表明，在3.5 wt . % NaCl溶液中，所制备的超疏水E-SiO2 / PDMS薄膜对MS基体具有高达99.99 %的缓蚀效率。

本工作集中在利用简单的方法和巧妙的成分制备出能够抵抗冰粘附的有效滑液灌注多孔表面( SLIPSs )。首先，合成了聚甲基丙烯酸甲酯( PMMA )、聚倍半硅氧烷端基功能化PMMA ( POSS- ef- PMMA )和聚二甲基硅氧烷嵌段PMMA ( PDMS-b- PMMA )。其次，微米尺寸的孔隙排列在三层蜂窝状阵列中，厚度为ca。用呼吸图( BF )法分别在这3种浇铸聚合物薄膜的每个表面引出10个 μm。将聚二甲基硅氧烷( PDMS )、聚氢甲基硅氧烷( PHMS )和十六烷( HD )单独渗入多孔基体后，形成典型的SLIPS。PDMS-b-聚甲基丙烯酸甲酯( PMMA )基体对PDMS具有优先亲油性，使所得SLIPS具有更好的抗冰性。然而，HD诱导的SLIPSs在3 μ L水滴的6 °滑动角下表现出最低的抗冰性能，最低的冰附着力范围为40.8 ~ 46.3   kPa，在不改变冰附着力的情况下，抗30次以上结冰/除冰循环的抗冰性能最为稳健。这种有效的防冰性能是由于HD与水接触时具有较好的液体性质，而HD在冷冻条件下具有较好的固相性，可降低HD与水或冰的界面摩擦磨损。

开发集自修复、自清洁、高效分离功能于一体的分离材料，对于含油废水和溢油的修复具有重要意义和挑战性。本工作发展了一种制备具有自修复超疏水性能的聚酰亚胺( PI )纳米纤维膜的简易方法。所设计的膜对一系列油水混合物和油包水乳液具有显著的分离效率。此外，由于PI膜与聚二甲基硅氧烷/十八胺( PDMS / ODA )涂层的协同环境稳定性，该膜在恶劣环境出良好的适应性。特别令人感兴趣的是，所制备的膜具有优异的自愈和自清洁能力，具有多功能集成。这些特性使膜成为一种在现实环境中高效油水分离的理想分离材料。