纳米压印

Direct imprinting of ordered and dense TiO 2 nanopore arrays by using a soft template for photovoltaic applications

ty10086 提交于 周四, 08/26/2021 - 13:41
Abstract(#br)Highly ordered and dense TiO 2 nanopore arrays are directly nanoimprinted on a transparent conductive glass substrate by using a polymethylmethacrylate/polydimethylsiloxane (PMMA/PDMS) composite soft template, which is replicated from an anodic aluminum oxide (AAO) replica mold. Results indicate that heat infiltration under vacuum conditions can ensure complete filling of PMMA into the AAO pores, and that free-standing PMMA nanorods with an aspect ratio more than 5 can be obtained by adjusting the AAO pore depth based on a freeze-drying technique.

提出仿壁虎足底的三级毛发结构及其紫外纳米压印制备

ty10086 提交于 周三, 08/25/2021 - 16:38
为了将紫外纳米压印法应用于制作仿壁虎脚掌上的细毛,将毛的形状设计成直形,使其易于从模具中释放出来。尖端分枝脱落的毛的长度设计为短,防止其聚集。在这些限制条件下,考虑到由于目标表面粗糙而产生的凹凸性,提出了一种由根毛、中间毛和尖毛组成的三级毛发结构,而不是由壁虎的集束和唾沫组成的二级毛发结构,使尖毛容易与凹凸表面接触。采用高精度三维立体光刻技术制作了由基座和毛发组成的母体。将此母体转移到PDMS上得到聚二甲基硅氧烷( PDMS )模具,利用此模具进行紫外纳米压印,成功地制备了光固化树脂制成的细毛发。该方法的优点是,由于3D光刻能够实现高长径比复杂结构的掌握,即不需要在根部和尖端分别进行两次纳米压印,因此可以通过单根纳米压印来制备三级毛发。证实了紫外纳米压印法制备的细发具有粘合力。

提出仿壁虎足底的三级毛发结构及其紫外纳米压印制备

ty10086 提交于 周三, 08/25/2021 - 16:11
为了将紫外纳米压印法应用于制作仿壁虎脚掌上的细毛,将毛的形状设计成直形,使其易于从模具中释放出来。尖端分枝脱落的毛的长度设计为短,防止其聚集。在这些限制条件下,考虑到由于目标表面粗糙而产生的凹凸性,提出了一种由根毛、中间毛和尖毛组成的三级毛发结构,而不是由壁虎的集束和唾沫组成的二级毛发结构,使尖毛容易与凹凸表面接触。采用高精度三维立体光刻技术制作了由基座和毛发组成的主模架。将此母体转移到PDMS上,得到聚二甲基硅氧烷( PDMS )模具。我们利用这种模具进行紫外纳米压印,成功地制作了光固化树脂制成的细毛。该方法的优点是,由于3D光刻能够实现高长径比复杂结构的掌握,即不需要在根部和尖端分别进行两次纳米压印,因此可以通过单根纳米压印来制备三级毛发。证实了紫外纳米压印法制备的细发具有粘合力。