Selective ozone treatment of PDMS printing stamps for selective Ag metallization: A new approach to improving resolution in patterned flexible/stretchable electronics

Abstract(#br)Hypothesis(#br)Selective ozone treatment of Polydimethylsiloxane (PDMS) print-stamps may facilitate local de-wetting of Krytox®1506 oil; the resulting printed pattern can be used as a masking liquid during roll-to-roll vacuum-metallization, exemplified with Ag. This novel method may exploit high-throughput manufacture without chemical etchants or elevated temperatures for thin-film electronics.(#br)Experiments(#br)The mechanism for selective wetting arose from O 3 treatment of PDMS through a shadow-mask to vary surface-energy due to formation of polar silanol (Si-OH) replacing surface methyl groups leading to contact angle reduction from 40°-9° for oil on PDMS. Oiled PDMS was (1) metalized itself and (2) used as a stamp to print onto polyethylene-terephthalate, consisting of oil pick-up/de-wetting/transfer-to-substrate/metallization.(#br)Findings(#br)Ag (520–568 nm) thick was deposited outside oiled regions, surpassing ~20 μm resolution of commercial printing. On metalized PDMS, minimum line widths were 2.6 μm (with 10 μm edge-grading from centrifugal oil spreading) or widths of 24 μm (no Ag grading) following spin-coating/roll-coating oil respectively. The progressive effect of thinning oil via five successive stamp-to-substrate impressions, produced line widths of 14 μm (with graded edge of 7.6 μm via spreading from stamp-substrate compression). Developments may reduce reliance on laser engraving/photocuring, and could enhance micro-contact printing through liquid dynamics vs . topographical relief structures.